Silane, Sioplas, Aerial Cable manufacturer / supplier in China, offering Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv, Black XLPE Compound for Mv Power Aerial Cable, Thermoplastic Semi-Conductive Shielding Compound and so on.

(/ )

Supplier Homepage Product Cross-linked Poly Ethylene (XPE) Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv

Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv

FOB Price: Get Latest Price
Min. Order: 1 Ton
Port: Shanghai, China
Production Capacity: 60000mt/Year
Payment Terms: L/C, T/T, D/P

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: YJW-35
  • HS Code: 39019090
Product Description
Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv

Black Silane-XLPE Compound of Sioplas Method for Aerial Cables
201C                                               
Explanations  
It is a type of warm water cross linking silane-xlpe compound applied for aerial wires and cables (up to 10kV) and has the following advantages: good electrical insulation properties, excellent anti-aging properties and tensile strength, the highest continuous working temperature is 90ºC; it has excellent low-temperature brittleness properties and anti-UV ability.
Specifications  
Black Silane-XLPE Compound of Sioplas Method for aerial wires and cables up to 10kV.
Physical and Electrical properties
No.Experiment ItemsTest MethodUnitTypical Value
1Tensile strengthGB/T 1040MPa24
2Elongation at breakGB/T 1040%450
3Brittleness temperature
-76ºC,30pieces
GB/T 5470Pieces0
4Aging
135ºC,168h
Change of tensile strengthGB/T 2951.2-1997%+2
Change of elongation at break%-3
5Thermal extension
200ºC,0.2MPa, 15min
Elongation  under loadGB/T 2951.5-1997/ GB/T 1040%50
Permanent deformation after cooling%0
6Gel contentJB/T 10437-2004%65
7Dielectric constant 50HZ, 20ºCGB/T 1409 2.2
8Dielectric loss factor 50Hz, 20 ºCGB/T 1409 3×10-4
9DC Volume resistivity 20 ºCGB/T 1410Ω.m1×1015
10Dielectric strengthGB/T 1408.1-1999MV/m38
 
Processing Techniques
Melt extrusion temperatures in the range of 150ºC-220ºC are recommended, the specific temperature should be adjusted by actual operation condition.
Cross-linking rate 
Cross-linking condition and time of the hot set elongation to 100%( 1 mm thick samples): vapor or water bath at 90ºC for 45min or at 80ºC for 90min.
Storage and transport   
It should be vacuum packed by the aluminium foil / polyethylene complex film bag for inner and PP woven bag / PE / Kraft paper bag for outer. The A and B groups are kept in different bags, net weight of A group is(23.75±0.02)kg and B group(1.25±0.02)kg, negative tolerance of each-ton material is not allowed. Besides, other packaging agreed on by both manufacturers and clients can be used.
Keep away from sunshine, rain and soaking during transport. Store in the clean, dry and ventilated warehouses; Storage temperature should not be below 0ºC.
Valid period is 6 month while it must be used out in 8 hours after the inner packaging is opened.

Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv

Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv
Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv
Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv
Send your message to this supplier
Avatar
Ms. Jess
*From:
To: Ms. Jess
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category