Power Cable, Medium Voltage, XPE manufacturer / supplier in China, offering Peroxide XLPE Compound for 10 Kv, Black XLPE Compound for Mv Power Aerial Cable, Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv and so on.

(/ )

Supplier Homepage Product Cross-linked Poly Ethylene (XPE) Peroxide XLPE Compound for 10 Kv

Peroxide XLPE Compound for 10 Kv

FOB Price: Get Latest Price
Min. Order: 1,000 kg
Port: Shanghai, China
Payment Terms: L/C, T/T, D/P

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: YJ-10
  • Conductor Type: Stranded
  • Sheath Material: PVC
  • Material Shape: Compound Granuel
  • Type: Insulated
  • Application: Insulation for Cable
  • Insulation Material: XLPE
  • HS Code: 39019090
Product Description
Peroxide XLPE Compound for 10 KvIt is made by mixture, plasticization and granulation with the low-density polyethylene as the basic resin mixed with cross linking agent and other additives. It doesn't contain harmful substances like heavy metal and has excellent mechanical, electrical and heat aging properties with the stable techniques properties as well as smooth surface. It is used as the insulation for MV Power Cable.
Specifications  
YJ-10   XLPE Compound insulation for MV cable up to 10kV
Physical and Electrical Properties
No.Experiment ItemTesting MethodUnitTypical value
1DensityGB/T1033-86g/cm30.921
2Tensile strengthGB/T1040-92MPa23
3Elongation at breakGB/T1040-92%530
 
 
4
Hot set elongation
0.2 MPa 15min
 
Elongation under load %55
Permanent deformation after cooling %-2
 
5
Aging
135ºC ,168h
Change of tensile properties %9
Change of elongation properties %5
6Gel content %85
7Brittle temperature -76ºCGB/T 5470Pieces0
8Resistance to environmental stress cracking h1200
9Dielectric constant 20ºC,50HZGB/T 1409-88/2.20
10Dissipation factor 20ºC,50HZ     GB/T 1409-88/2×10-4
11DC Volume resistivity 20ºCGB/T 1410-89Ω·m9×1014
12Dielectric strength 20ºCGB/T 1408.1MV/m39
(1)It is tested according to the specifications of the latest version of China National Standard.
(2) The data is from the sample of plate vulcanizing press (180 ºC and 15 min) and should not be used as the standard.
 
Impurity requirements 
YJ-10 meets the strict standard in the cleaning aspect. Throughout production process, loading, processing and packaging are all strictly controlled and performed in an airtight environment. The sample is tested by laboratory impurity detector in the production process periodically, and the impurity content of 1 kg-sampling complies with the following requirements: impurity particles with 0.175~0.250mm diameter no more than 5; no one larger than 0.250mm.
Processing techniques
Over a broad range of processing techniques, YJ-10 can still provide excellent extrusion capacity and smooth surface. For optimum results, melt extrusion temperatures in the range of 100 ºCto 120 ºC are recommended.
Storage and transport
Keep away from sunshine and rain during the transport, and store in clean, dry and ventilated warehouse. The product may be stored for up to 6 months without opening at normal temperature.
Peroxide XLPE Compound for 10 Kv
Peroxide XLPE Compound for 10 Kv
Peroxide XLPE Compound for 10 Kv
Peroxide XLPE Compound for 10 Kv
 
Send your message to this supplier
Avatar
Ms. Jess
*From:
To: Ms. Jess
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category