Silane, Sioplas, Aerial Cable manufacturer / supplier in China, offering Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv, Black XLPE Compound for Mv Power Aerial Cable, Thermoplastic Semi-Conductive Shielding Compound and so on.

(/ )

Supplier Homepage Product Cross-linked Poly Ethylene (XPE) Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv

Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv

FOB Price: Get Latest Price
Min. Order: 1 Ton
Port: Shanghai, China
Production Capacity: 60000mt/Year
Payment Terms: L/C, T/T, D/P

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: YJWG-10
  • HS Code: 39019090
Product Description
Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv
It is made by mixture, plasticization and granulation with the low-density polyethylene as the basic resin mixed with carbon black master batch, cross linking agent and other additives. It doesn't contain harmful substances like heavy metal and has excellent mechanical, electrical and heat aging properties with the stable technique as well as smooth surface. It is used as the insulation of aerial cable.
Specifications  
YJW-10    XLPE Compound insulation for aerial cable up to 10kV
Physical and Electrical Properties
No.Experiment ItemTesting MethodUnitTypical value
1DensityGB/T1033-86g/cm30.921
2Tensile strengthGB/T1040-92MPa19
3Elongation at breakGB/T1040-92%490
 
4
4
Hot set elongation
0.2 MPa 15min
 
Elongation under load %55
Permanent deformation after cooling %-2
 
5
Aging
135ºC ,168h
Change of tensile properties %12
Change of elongation properties %10
6Gel content %80
7Resistance to environmental stress cracking F50 hpass
8Brittle temperature -76ºCGB/T 5470Pieces0
9Dielectric constant 20ºC,50HZGB/T 1409-88/2.20
10Dissipation factor 20ºC,50HZ     GB/T 1409-88/5×10-4
11DC Volume resistivity 20ºCGB/T 1410-89Ω·m4×1014
12Dielectric strength 20ºCGB/T 1408.1MV/m39
 (1)It is tested according to the specifications of the latest version of China National Standard
(2) The data is from the sample of plate vulcanizing press (180 ºC and 15 min) and should not be used as the standard
Processing techniques   
Over a broad range of processing technique, YJW-10 can still provide excellent extrusion capacity and smooth surface. For optimum results, melt extrusion temperature in the range of 100 ºCto 120 ºC are recommended.
Storage and transport  
Keep away from sunshine and rain during the transport, and store in clean, dry and ventilated warehouse. The product may be stored for up to 6 months without opening at normal temperature.
Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv

Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv
Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv
Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv
 
Send your message to this supplier
Avatar
Ms. Jess
*From:
To: Ms. Jess
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category