XLPE, Insulator, Conductor manufacturer / supplier in China, offering Strippable Semi-Conductive Crosslinkable Insulator Screen Material, Black XLPE Compound for Mv Power Aerial Cable, Silane XLPE Compound of Sioplas Method for Aerial Wire and Cable up to 10kv and so on.

(/ )

Supplier Homepage Product Semi-conductive compound Strippable Semi-Conductive Crosslinkable Insulator Screen Material

Strippable Semi-Conductive Crosslinkable Insulator Screen Material

FOB Price: Get Latest Price
Min. Order: 1 Ton
Port: Shanghai, China
Production Capacity: 20000tons/Year
Payment Terms: L/C, T/T

Request a custom order and have something just for you!

Send Customized Request
Basic Info
  • Model NO.: PYJBJ-35
  • Type: Insulation Sleeve
  • Material: Resin
  • Classification: Hybrid Insulation Materials
  • Color: Black
  • Transport Package: 500kgs/Bag, 1ton/Pallet
  • HS Code: 39013000
  • Application: Insulators
  • Chemistry: Hybrid Insulation
  • Maximum Voltage: <35kv
  • Certification: UL, ISO9001
  • Trademark: WANMA
  • Origin: Hangzhou
Product Description
Strippable Semi-Conductive Crosslinkable Insulator Screen Material
Properties of Strippable semi-conductive crosslinkable conductor screen material up to 35kv.
No.ItemUnitStandard
PYJBJ
1Densityg/cm3≤1.2
2Tensile strength MPa≥10.0
3Elongation at break%≥200
4Test conditions of the air thermal aging test:
Thermal aging temperature
Duration
Change in tensile strength≤
Change rate of the elongation at break≤
 
ºC
h
%
%
 
135±2
168
±30
±30
5Impact catalytic test conditions:
Test temperature
Impact catalytic properties
 
ºC
Fail
 
-40
≤15/30
6Hot set test conditions:
Temperature
Mechanical load
Load Time
Load elongation
Permanent deformation after cooling
 
ºC
Mpa
min
%
%
 
200±2
0.2
15
≤100
≤15
7volume resistivity at 20 ºCΩ.cm≤100
8volume resistivity at 90 ºCΩ.cm≤2500
9Test conditions of volume resistivity after thermal aging in air:
Aging temperature
Duration
volume resistivity at 90 ºC
 
ºC
h
Ω.cm
 
100±2
168
≤500
10Strippable strength
(23ºC)
N/cm10-45
11The air thermal aging strippable strength
Strippable strength after thermal aging in air test conditions:
Aging temperature
Duration
N/cm
ºC
h
10-45
100±2
168

Strippable Semi-Conductive Crosslinkable Insulator Screen Material
Strippable Semi-Conductive Crosslinkable Insulator Screen Material
Strippable Semi-Conductive Crosslinkable Insulator Screen Material
Strippable Semi-Conductive Crosslinkable Insulator Screen Material
 
Send your message to this supplier
Avatar
Ms. Jess
*From:
To: Ms. Jess
*Message:

Enter between 20 to 4,000 characters.

This is not what you are looking for? Post a Sourcing Request Now

Find Similar Products By Category